Custom Bumpon products may require a qualifying minimum quantity and/or a one time set-up charge. Call your local 3M sales
representative for more information.
(3)
3M
™
Bumpon
™
Protective Products
- Molded Shapes - Colored and Clear
Series SJ5000
•
SJ5300
•
SJ5400
•
SJ5500
•
SJ5700
•
SJ6100
Typical Physical Properties and Performance Characteristics
Note:
he following technical information and data should be considered representative or typical only and should
T
not be used for specification purposes.
Hardness, Shore M
Resilience, %
Kinetic Coefficient of Friction (Mk)
(Dependent on Test Surface)
1
3M Test Method
4
ASTM-D2240
ASTM-D2632,
0.125" sample
ASTM-D1894
Stainless Steel
Glass
Formica
®
laminate
Wood
ASTM-C501
3M™ Bumpon™ Protective Products
SJ5000
SJ5500
SJ5300
SJ5700
SJ5400
SJ6100
72
30
75
5
72
30
>1
>1
0.9-1.4
0.9-1.4
1.7-1.9
>1
>1
0.9-1.4
0.9-1.4
0.13
>1
>1
0.9-1.4
0.9-1.4
1.7-1.9
Abrasion Resistance
(Taber H18, 1kg)
g/1000 cycles
2
Tensile, lbs/in
2
(MPa)
2
Elongation,%
2
Dielectric Strength,
volts/mil
2
Stain Resistance
3
ASTM-D412, Die A
ASTM-D412, Die A
ASTM-D1000
3M-24 hours @ 158°F
against white paint
7 days exposed to UV.
UL-94HB
600 (4.1)
100
200
No
Staining
Pass;
UL Recognized
740 (5.1)
65
370
No
Staining
Not UL
Recognized
600 (4.1)
100
200
No
Staining
Pass;
UL Recognized
Flammability Listing
Application Temperature
Service Temperature
Solvent and Fuel Resistance
3
5°C (40°F) to 52°C (125°F)
Constant:
Intermittent:
24 hour immersion
5% Detergent in water
25% Ammonia in water
Bleach
Hydrochloric Acid
(1 Normal Solution)
Diesel Fuel
Auto Oil
Isopropyl Alcohol
Heptane
Toluene (Toluol)
Lacquer Thinner
-34°C (-30°F) to 66°C (150°F)
Up to 107°C (225°F)
No Apparent Effect
No Apparent Effect
No Apparent Effect
No Apparent Effect
No Apparent Effect
No Apparent Effect
Slight Swelling
Slight Swelling
Considerable Swelling
Considerable Swelling
Notes:
1
Two important laws of friction applicable to Bumpon products are: (1) Friction is independent of the area of contact between solids and (2) friction is
proportional to the load between solid surfaces. Thus, if the load (weight) is doubled the force required to cause sliding is also double. This is expressed
mathematically as follows: Sliding Force = Mk x weight.
2
These properties were run on sheet material from the same materials as the individual Bumpon products
3
Reference test for 24 hours. Results may vary for different product application conditions.
4
When ASTM method is listed, data was collected in accordance with ASTM test method.
(4)
3M
™
Bumpon
™
Protective Products
- Molded Shapes - Colored and Clear
Series SJ5000
•
SJ5300
•
SJ5400
•
SJ5500
•
SJ5700
•
SJ6100
Relative Adhesive Performance Characteristics
Note:
he following technical information and data should be considered representative or typical only and should
T
not be used for specification purposes.
Adhesive:
Initial Adhesion
Low Surface Energy:
High Surface Energy:
Adhesion (Peel)
Low Surface Energy:
High Surface Energy:
Static Shear
25°C (75°F):
49°C (120°F):
70°C (158°F):
Dynamic Shear:
Solvent Resistance:
SJ5000
SJ5500
SJ5700
Natural Rubber
R-30
Good
Good
Good
Good
Excellent
Good
Poor
Good
Good
3M™ Bumpon™ Protective Products
SJ5300
SJ5400
Acrylic
A-20
Poor
Fair
Poor
Good
Excellent
Excellent
Excellent
Excellent
Excellent
SJ6100
Synthetic Rubber
R-25
Excellent
Excellent
Excellent
Excellent
Excellent
Good
Fair
Good
Good
Adhesive Performance
Note:
he following technical information and data should be considered representative or typical only and should
T
not be used for specification purposes.
The following table on peel adhesion provide representative performance characteristics of the adhesive
systems used in the construction of 3M™ Bumpon™ Protective Products molded series products.
90° Peel Adhesion
Substrate:
Polypropylene
Polystyrene
ABS
Stainless Steel
Aluminum
SJ5000
SJ5500
SJ5700
Natural Rubber
R-30
25
25
25
22
22
*Peel Force, oz. Per 1/2 inch
3M™ Bumpon™ Protective Products
SJ5300
SJ5400
Acrylic
A-20
3
11
25
25
25
SJ6100
Synthetic Rubber
R-25
52
55
55
55
55
*
M Test Method TM-2011; 72 hour dwell, 1/2 inch wide samples pulled at 12 inches per minute. Testing completed using Bumpon Resilient Rollstock
3
products SJ5816, SJ6016, and SJ6216, which use the same adhesive system as the molded series products.