JARO high voltage series Multilayer Ceramic Capacitors are constructed by depositing alternative layers of ceramic dielectric materials and internal metallic electrodes, by
using advanced ceramic manufacturing technology, and co-firing into an indestructible homogeneous body, then completed with application of metal end terminations which
are fired on to assure that permanent connection of individual internal electrodes are in parallel.
The terminations are nickel-plated and then solder plated to give the chip capacitors nickel-barrier terminations which have much better leaching resistance during soldering.
Reliable performances are built-in through exact formulation of dielectric powders, preparation of conductive paste, advanced automatic manufacturing, and strict quality
control to assure excellent control in dielectric thickness, electrode integrity, and electrode-to-termination continuity.
JARO offers the high performance MLCC of high voltage. There are five standard sizes 0805, 1206, 1210, 1808, and 1812 and ranging from 100V to 2KV in COG and X7R
characteristics.
RECOMMENDED APPLICATIONS
Modems
LAN/WAN Interface
Power Supplies
Telecom Devices
Industrial Controls
MECHANICAL DATA
Component outline:
CAPACITOR DIMENSIONS
Size
(L) Length
(W) Width
(E) Termination
mm
(in)
mm
(in)
mm
(in)
0805
2.00 ± 0.20
(.080 ± .008)
1.20 ± 0.20
(.050 ± .008)
0.50 ± 0.20
(.020 ± .008)
1206
3.20 ± 0.20
(.126 ± .008)
1.60 ± 0.20
(.063 ± .008)
0.50 ± 0.20
(.020 ± .008)
1210
3.20 ± 0.30
(.126 ± .012)
2.50 ± 0.30
(.100 ± .012)
0.50 ± 0.20
(.020 ± .008)
1808
4.50 ± 0.30
(.177 ± .012)
2.00 ± 0.20
(.080 ± .008)
0.64 ± 0.38
(.025 ± .015)
1812
4.50 ± 0.30
(.177 ± .012)
3.20 ± 0.30
(.126 ± .012)
0.64 ± 0.38
(.025 ± .015)
Dimensions are in millimeters, dimensions in parenthesis are in inches.
6600 Park of Commerce Blvd. • Boca Raton, FL 33487
Class I (COG) capacitors shall be conditioned for 96 ± 4hr by heating in a circulationg air oven at a temperature of 55 ± 2°C and a relative humidity not exceeding 20%.
The capacitor shall then be allowed to cool in a desiccator using a suitable desiccant, such as activated alumina or sillica gel, and shall be kept therein from the time of
removal from the oven to the beginning of the specified tests.
Class II (X7R, Z5U, Y5V) capacitors shall be made a special pre-conditioning before a test or a sequence of tests under the following conditions: Exposure at 150 ±
10°C for 1 hr, followed by setting the capacitor at room temperature for 24 ± 1 hr.
*2.
Capacitance is within specified tolerance; measured 1000 hours after date of manufacture because of capacitance aging of class II capacitor.
TYPICAL PERFORMANCE CURVES
6600 Park of Commerce Blvd. • Boca Raton, FL 33487
At least 75% of termination area should be well tinned.
No visible damage.
At least 75% of termination should be covered by solder.
No visible damage.
COG (1BCG)
X7R (2R1)
∆C/C
≤
± 0.5%, or ± 0.5pF
≤
+10%
whichever is greater
-5%
No visible damage.
COG (1BCG)
X7R (2R1)
∆C/C
≤
± 1%, or ± 1pF
≤
+10%
whichever is greater
D.F.
≤
1.5 x initial requirement
I.R.
≥
0.25 x initial requirement
No visible damage.
COG (1BCG)
X7R (2R1)
∆C/C
≤
± 2%, or ± 1pF
≤
+20%
whichever is greater
D.F.
≤
2.0 x initial requirement
≤
1.5 x initial requirement
I.R.
≥
0.25 x initial requirement
No visible damage.
COG (1BCG)
∆C/C
D.F.
I.R.
≤
± 2%, or ± 1pF
whichever is greater
≤
2.0 x initial requirement
Rapid Change of
Temperature
*2
IEC 384-10 4.12 /JIS C 5102 9.3
-55C to +125°C, 5 cycles (COG, X7R)
Duration: 30 mins.
Recovery: 6~24 hrs. (COG)
24 ± 2 hrs. (X7R)
IEC 384-10 4.15
1000 hrs. at maximum temperature applied
with 2.0 x U
R
(≤ 250V), 1.5 x U
R
(≤ 1KV),
1.2 x U
R
(≤ 2KV)
Recovery: 6~24 hrs. (COG)
24 ± 2 hrs. (X7R)
Endurance
(Life Test)
*3
Humidity Test
(Damp heat,
steady state)
*4
IEC 384-10 4.14 /JIS C 5102 9.5
500 hrs. at 40 ± 2°C, 90-95% RH
Recovery: 6~24 hrs. (COG)
24 ± 2 hrs. (X7R)
X7R (2R1)
≤
+10%
≤
1.5 x initial requirement
≥
0.25 x initial requirement
Adhesion
IEC 384-10 4.8 /JIS C 5102 8.11.2
Capacitors mounted on a substrate, a force of 5N
applied perpendicular to the plane of substrate and
parallel the line joining the centre of terminations
for 10 ± 1 secs.
No visible damage.
*1~4: Class II (X7R, Z5U, Y5V) capacitors shall be made a special pre-conditioning before a test or a sequence of tests under the following conditions: Exposure at 150 ±
10°C for 1 hr, followed by setting the capacitor at room temperature for 24 ± 1 hr.
6600 Park of Commerce Blvd. • Boca Raton, FL 33487
LG Display昨日发布的2018年第一季度财报再一次说明了面板行业寒冬正在到来。该财报指出，LG Display2018年第一季度营业亏损达980亿韩元，出现近6年来的首次运营亏损。此前发布的友达光电、京东方财报也说明，受液晶面板价格迅速下滑影响，友达光电、京东方的营收和利润也出现了同比下跌的现象。从去年第三季度以来，液晶面板价格持续下滑，因为去年6代线、8.5代线等新增产能的逐渐释放，液...[详细]
在电子制造业领域影响力广泛的专业精品展会——第二十八届中国国际电子生产设备暨微电子工业展(NEPCON China 2018)于2018年4月24日在上海世博展览馆盛大开幕。 作为行业久富盛誉的品质强展，NEPCON China 2018依托国内外电子制造领域前沿技术，全面覆盖SMT表面贴装、测试测量、焊接与点胶喷涂、电子新材料、智慧工厂等各环节革新设备、材料和系统集成方案，联手FUJI、P...[详细]
模拟电子
京公网安备 11010802033920号
Copyright © 2005-2026 EEWORLD.com.cn, Inc. All rights reserved
电子工程世界