Heat shrinkable sleeves
MATERIAL DESCRIPTION:
USE:
Thin wall, flame retarded radiation cross-linked polyolefin heat-shrinkable tubing,
assembled as organized cut sleeves in a “ladder” configuration. 3:1 shrink ratio.
Identification of wires and cables by computer-based printing onto sleeves.
Sleeves can also provide terminal insulation and strain relief. Suitable for many
commercial applications.
PRINT METHOD/RIBBON:
See document 411-121005 IDENTIFICATION PRINTER PRODUCT
RIBBON MATRIX for the recommended printer/product/ribbon
combination.
-30
C to +105
C (-22
F to +221
F).
White or yellow.
Burn time <1 minute (UL 224, all tubing flame test).
20% maximum on shrinking.
8MPa minimum (ASTM D2671).
150% minimum (ASTM D2671).
56 day incubation (ISO 846B)
–
tensile strength, ultimate elongation and
Dielectric strength maintained after testing.
19.7MV/m minimum.
40
C (104
F).
Print legible after 20 rubs (SAE AS5942)
Print legible after 30 strokes (MIL-STD-202F, method 215J)
SERVICE TEMPERATURE:
COLORS:
FLAMMABILITY:
LONGITUDINAL CHANGE:
TENSILE STRENGTH:
ULTIMATE ELONGATION:
MOLD GROWTH:
DIELECTRIC STRENGTH:
MAXIMUM STORAGE
TEMPERATURE:
PRINT PERMANENCE:
While TE Connectivity Ltd. has made every reasonable effort to ensure the accuracy of the information in this document, TE does
not guarantee that it is error-free, nor does TE make any other representation, warranty or guarantee that the information is
accurate, correct, reliable or current. TE reserves the right to make any adjustments to the information contained herein at any time
without notice. TE expressly disclaims all implied warranties regarding the information contained herein, including, but not limited
to, any implied warranties of merchantability or fitness for a particular purpose. The dimensions in this document are for reference
purposes only and are subject to change without notice. Specifications are subject to change without notice. Consult TE for the
latest dimensions and design specifications.
©2014 Tyco Electronics Corporation, a TE Connectivity Ltd. Company
TTDS-019 Issue 4
*Trademark. TE Connectivity, TE connectivity (logo), and TE (logo) are trademarks. Other logos, product and/or company names may be
trademarks of their respective owners.
If this document is printed it becomes uncontrolled.
DATA SHEET
Document number: TTDS-019
Issue: 4
Date: March 2014
RPS
Heat shrinkable sleeves
THREAT
TEST
24 hours at 23
C (73
F), SAE AS5942 (20 rubs)
24 hours at 23
C (73
F), SAE AS5942 (20 rubs)
24 hours at 23
C (73
F); SAE AS5942 (20 rubs)
24 hours at 23
C (73
F); SAE AS5942 (20 rubs)
EFFECT
Print legible
Print legible
Print legible
Print legible
Isopropyl Alcohol
Gasoline (unleaded)
Diesel Fuel, DF2
Auto Engine Oil, SF
10W-40 (SAE J 183, SAE J
300)
Motor Vehicle Brake Fluid,
SAE J 1703
Ethylene Glycol
Notes:
24 hours at 23
C (73
F); SAE AS5942 (20 rubs)
24 hours at 23
C (73
F); SAE AS5942 (20 rubs)
Print legible
Print legible
See TE specification RW2510 for full RPS performance & dimensional details.
Some types of neoprene insulation used in jackets contain additives that can migrate to the surface and
discolor the polyolefin RPS sleeves. Any discoloration is dependent on the composition of the neoprene,
combined with application conditions. Users should independently evaluate the suitability of RPS sleeves
for applications involving neoprene-jacketed cables.
©2014 Tyco Electronics Corporation, a TE Connectivity Ltd. Company
TTDS-019 Issue 4
*Trademark. TE Connectivity, TE connectivity (logo), and TE (logo) are trademarks. Other logos, product and/or company names may be
trademarks of their respective owners.
If this document is printed it becomes uncontrolled.
模拟与混合信号
京公网安备 11010802033920号
Copyright © 2005-2026 EEWORLD.com.cn, Inc. All rights reserved
电子工程世界