Materials
-12
Modified Fluoroelastomer
Product Facts
Heat-shrinkable, flexible,
fluid-resistant modified
fluoro-elastomer
■
Excellent resistance to long-
term fuel immersion
■
4
Molded Parts
Applications
TE -12 molded parts with
fluoroelastomers are
designed to be used in con-
junction with tubing made
from fluoroelastomers or
multi-conductor cable jack-
ets and a suitable adhesive
in System 200.
This system provides
excellent resistance to
elevated temperatures and
continuous fuel immersion.
Available in a wide range
of configurations, -12
molded parts will operate
from -55°C [-67°F] to 200°C
[392°F]. The standard color
is black.
Installation
-12 molded parts will shrink
on the application of heat
above 175°C [347°F].
Recommended installation
temperature: 220°C [428°F]
Operating Temperature Range
-55°C to 200°C
[-67°F to 392°F]
Available in:
Americas
■
Europe
■
Asia Pacific
■
4-29
Catalog 1654025
Revised 5-12
www.te.com
Dimensions are shown for
reference purposes only.
Specifications subject
to change.
Dimensions are in millimeters
unless otherwise specified.
USA: +1 (800) 522-6752
Canada: +1 (905) 475-6222
Mexico/C. Am.: +52 (0) 55-1106-0800
Latin/S. Am.: +54 (0) 11-4733-2200
Germany: +49 (0) 6251-133-1999
UK: +44 (0) 800-267666
France: +33 (0) 1-3420-8686
Netherlands: +31 (0) 73-6246-999
China: +86 (0) 400-820-6015
Materials
-12
(Continued)
Specifications/Approvals
Military
SAE-AS81765/4
Def. Stan. 59-97 Issue 3 Type DD (Europe)
BS-G-198-5-DD-P (Europe)
SAE-AS85049/ 140, 141, 142
(material designator D)
TE
RT-1312
—
—
—
Product Characteristics
Tensile strength
Ultimate elongation
2% secant modulus
Specific gravity
Heat aging for 168 h at 250°C [482°F]
Heat shock for 4 h at 300°C [572°F]
Low temperature flex at -55°C [-67°F]
Flammability (burn time)
Electric strength
—
Aviation fuel F40
Fluid resistance
Lubricating oil O-149
Hydraulic fluid H515
Specification Requirements
12.4 MPa (min.)
300% (min.)
70 MPa (max.)
1.95 (max.)
Ultimate elongation 250% (min.)
No dripping, cracking, or flowing
No cracking
30 s (max.)
8 MV/m (min).
0.5% (max.)
Tensile strength 11 MPa (min.)
Ultimate elongation 200% (min.)
Tensile strength 11 MPa (min.)
Ultimate elongation 200% (min.)
Tensile strength 11 MPa (min.)
Ultimate elongation 200% (min.)
Test Method
ISO 37
ISO 37
ASTM D 882
ISO 1183
ISO 188, ISO 37
ASTM D 2671
ASTM D 2671
ASTM D 635
IEC 243
ISO 62
ISO 1817
after immersion for 24 h at 23°C [73°F]
ISO 1817
after immersion for 24 h at 93°C [200°F]
ISO 1817
after immersion for 24 h at 93°C [200°F]
Physical
Thermal
Electrical
Water absorption
4-30
Catalog 1654025
Revised 5-12
www.te.com
Dimensions are shown for
reference purposes only.
Specifications subject
to change.
Dimensions are in millimeters
unless otherwise specified.
USA: +1 (800) 522-6752
Canada: +1 (905) 475-6222
Mexico/C. Am.: +52 (0) 55-1106-0800
Latin/S. Am.: +54 (0) 11-4733-2200
Germany: +49 (0) 6251-133-1999
UK: +44 (0) 800-267666
France: +33 (0) 1-3420-8686
Netherlands: +31 (0) 73-6246-999
China: +86 (0) 400-820-6015
京公网安备 11010802033920号
Copyright © 2005-2026 EEWORLD.com.cn, Inc. All rights reserved
电子工程世界