Adhesive Transfer Tapes with Adhesive 200MP
467MP
7955MP
9667MP
Technical Data
Product Description
468MP
467MPF
468MPF
7952MP
7962MP
7965MP 9172MP 9185MP
9668MP
May 2017
3M™ High Performance Acrylic Adhesive 200MP is a popular choice
for graphic attachment and general industrial joining applications. It
provides outstanding adhesion to metal and high surface energy
plastics. This adhesive provides some initial repositionability for
placement accuracy when bonding to plastics. It also performs well
after exposure to humidity and hot/cold cycles.
Up to 400⁰F short-term heat resistance
Excellent solvent resistance
Excellent shear strength to resist slippage and edge lifting
Construction
Information
Product
Adhesive Thickness
mils
(mm)
Liner Type
Liner Thickness
mils
(mm)
58# Polycoated Kraft Paper
(PCK)
4.2 mils
(0.11 mm)
58# Polycoated Kraft Paper
(PCK)
4.2 mils
(0.11 mm)
Polyester Film (PET)
Liner Color
467MP
2.3 mils
(0.06 mm)
468MP
5.2 mils
(0.13 mm)
467MPF
2.3 mils
(0.06 mm)
2.0 mils
(0.05 mm)
Polyester Film (PET)
468MPF
5.2 mils
(0.13 mm)
2.0 mils
(0.05 mm)
Liner Type
Liner Thickness
mils
(mm)
Liner Color
Product
Adhesive Thickness
mils
(mm)
3M™ Adhesive Transfer Tapes with Adhesive 200MP
467MP, 468MP, 467MPF, 468MPF, 7952MP, 7955MP, 7962MP, 7965MP,
9172MP, 9185MP, 9667MP, 9668MP
Construction
Information
(continued)
2.3 mils
(0.06 mm)
78# Polycoated Kraft Paper
(PCK)
5.7 mils
(0.15 mm)
78# Polycoated Kraft Paper
(PCK)
5.7 mils
(0.15 mm)
9667MP
9668MP
5.2 mils
(0.13 mm)
Product
Adhesive
Thickness
mils
(mm)
Liner 1 Type
Liner 1
Thickness
mils
(mm)
58# Polycoated
Kraft Paper (PCK)
4.2 mils
(0.11 mm)
58# Polycoated
Kraft Paper (PCK)
4.2 mils
(0.11 mm)
78# Polycoated
Kraft Paper (PCK)
5.7 mils
(0.15 mm)
78# Polycoated
Kraft Paper (PCK)
5.7 mils
(0.15 mm)
High Density
Polyethylene Film
(HDPE)
3.0 mils
(0.08 mm)
High Density
Polyethylene Film
(HDPE)
3.0 mils
(0.08 mm)
Liner 1 Color
Liner 2 Type
Liner 2
Thickness
mils
(mm)
58# Polycoated
Kraft Paper (PCK)
4.2 mils
(0.11 mm)
58# Polycoated
Kraft Paper (PCK)
4.2 mils
(0.11 mm)
58# Polycoated
Kraft Paper (PCK)
4.2 mils
(0.11 mm)
58# Polycoated
Kraft Paper (PCK)
4.2 mils
(0.11 mm)
58# Polycoated
Kraft Paper (PCK)
4.2 mils
(0.11 mm)
Liner 2 Color
7952MP
2.3 mils
(0.06 mm)
7955MP
5.2 mils
(0.13 mm)
7962MP
2.3 mils
(0.06 mm)
7965MP
5.2 mils
(0.13 mm)
9172MP
2.3 mils
(0.06 mm)
9185MP
5.2 mils
(0.13 mm)
58# Polycoated
Kraft Paper (PCK)
4.2 mils
(0.11 mm)
Note:
The thickness listed is based on a calculation from manufacturing controlled adhesive coat weights using
a density of 1.012 g/cc. While past data pages have listed nominal thicknesses, the coat weight (and
theoretical caliper) has not changed.
2
3M™ Adhesive Transfer Tapes with Adhesive 200MP
467MP, 468MP, 467MPF, 468MPF, 7952MP, 7955MP, 7962MP, 7965MP,
9172MP, 9185MP, 9667MP, 9668MP
Note: All of the following technical information and data should be considered
representative or typical only and should not be used for specification purposes.
Typical Physical
Properties and
Performance
Characteristics
I.
Adhesion Peel:
ASTM D-3330 (Modified)
a. Stainless Steel and 2 mil Aluminum Foil Backing
15 minute dwell
(± 5 minutes)
Product
2.3 mil
products
(467MP,
467MPF,
7952MP,
7962MP,
9172MP,
9667MP)
5.2 mil
products
(468MP,
468MPF,
7955MP,
7965MP,
9185MP,
9668MP)
90⁰
72 hour
dwell
158F
90⁰
72 hour dwell RT
90⁰
180⁰
49 oz/in
14 N/25 mm
92 oz/in
26 N/25 mm
77 oz/in
21 N/25 mm
153 oz/in
43 N/25 mm
55 oz/in
15 N/25 mm
108 oz/in
30 N/25 mm
139 oz/in
39 N/25 mm
183 oz/in.
51 N/25mm
b. Adhesion to Other Surfaces: ASTM D3330 modified (90° peel, 2
mil aluminum foil backing with 72 hour dwell)
2.3 mil products
(467MP, 467MPF, 7952MP,
7962MP, 9172MP, 9667MP)
5.2 mil products
(468MP, 468MPF, 7955MP,
7965MP, 9185MP, 9668MP)
Substrate
Aluminum
ABS
Acrylic
Glass
Polycarbonate
Rigid PVC
(unplasticized)
oz/in
64
22
64
90
71
40
N/25 mm
18
06
18
25
20
11
oz/in
84
27
81
112
88
46
N/25mm
23
08
23
31
24
13
3
3M™ Adhesive Transfer Tapes with Adhesive 200MP
467MP, 468MP, 467MPF, 468MPF, 7952MP, 7955MP, 7962MP, 7965MP,
9172MP, 9185MP, 9667MP, 9668MP
Typical Physical
Properties and
Performance
Characteristics
(continued)
II.
Static Shear Strength
Weight
1000 grams
1000 grams
1000
500
400
200
Minutes
10,000+
10,000+
10,000+
10,000+
2284
10,000+
Temperature
Size
72⁰ (23⁰C)
1″ x 1″
50%RH
158⁰F (70⁰C)
1″ x 1″
50% RH
1″ x 1″
200⁰F (93⁰C)
50% RH
1″ x 1″
350⁰F (177⁰C)
50% RH
1″ x 1″
450⁰F (232⁰C)
50% RH
1″ x 1″
450⁰F (232⁰C)
50% RH
*Test terminated at 10,000 minutes
III.
Adhesion Retention after Immersion and Exposure
(percent retention)
Control is 24 hour RT dwell on stainless
steel, 2 mil foil backing, 90⁰ peel, 12 ipm. ** Adhesion values
above 80 oz/1” is considered to be a permanent bond.
2.3 mil products
(467MP, 467MPF,
7952MP, 7962MP,
9172MP, 9667MP)
87 (25)
72 (20)
70 (20)
70 (20)
66 (19)
127 (36)
87 (25)
87 (25)
109 (31)
104 (29)
5.2 mil products
(468MP, 468MPF,
7955MP, 7965MP,
9185MP, 9668MP)
94 (27)
80 (23)
82 (23)
95 (27)
86 (24)
162 (46)
95 (27)
122 (35)
150 (42)
158 (45)
All Values in oz/1″ width & (N/25mm)
Control - Adhesion to Stainless Steel
Gasoline – 1 hour RT immersion
MEK – 1 hour RT immersion
Weak Acid – 4 hour RT immersion
Weak Base – 4 hour RT immersion
Oil (10W30) – 72 hour, 120⁰F (49⁰C)
immersion
Water – 100 hours, 70⁰F (21⁰C)
Salt Water (5%) – 72 hours, 70⁰F
(21⁰C)
Warm/Humid – 7 days, 90⁰F (32⁰C)
and 90% relative humidity
UV Conditions - ASTM G-154 Cycle 1,
for 2000 hours
Temperature Cycling – 4 Cycles @
(4 hours, 158⁰F (70⁰C); 4 hours, -20⁰F
(-29⁰C); 16 hours, 70⁰F (21⁰C))
112 (32)
139 (39)
4
3M™ Adhesive Transfer Tapes with Adhesive 200MP
467MP, 468MP, 467MPF, 468MPF, 7952MP, 7955MP, 7962MP, 7965MP,
9172MP, 9185MP, 9667MP, 9668MP
Environmental
Performance
Humidity Resistance –
High humidity has a minimal effect on
adhesive performance. Bond strength shows no significant
reduction after exposure for 7 days at 90⁰F (32⁰C) and 90%
relative humidity.
UV Resistance –
When properly applied, nameplates and
decorative trim parts are not adversely affected by outdoor
exposure.
Water Resistance –
Immersion in water has no appreciable
effect on the bond strength. After 100 hours at room temperature,
the high bond strength is maintained.
Temperature Cycling Resistance –
High bond strength is
maintained after cycling four times through:
4 hours at 158⁰F (70⁰C)
4 hours at -20⁰F (-29⁰C)
16 hours at 73⁰F (22⁰C)
Chemical Resistance –
When properly applied, nameplate and
decorative trim parts will hold securely after exposure to
numerous chemicals including oil, mild acids and alkalis.
Bond Build-up:
The bond strength of 3M™ High Performance
Acrylic Adhesive 200MP increases as a function of time and
temperature
Temperature/Heat Resistance:
3M™ High Performance Acrylic
Adhesive 200MP is usable for short periods (minutes, hours) at
temperatures up to 400⁰F (204⁰C) and for intermittent longer
periods (days, weeks) up to 300⁰F (149⁰C).
Lower Temperature Service Limit:
The glass transition
temperature for 3M™ High Performance Acrylic Adhesive 200MP
is -40°F (-40°C). Many applications survive below this
temperature (factors affecting successful applications include:
materials being bonded, dwell at RT before cold exposure, and
stress below the TG, [i.e. expansion / contraction stresses,
impact]). Optimum conditions are: bonding high surface energy
materials, longer time at RT before cold exposure, and little or no